AlGaN Back Barrier Aids HEMT Scaling

Forming double-heterostructure FETs with an AlGaN barrier improves electron confinement, leading to a higher drain bias.




RESEARCHERS at the Institute of Electronics, Microelectronics and Nanotechnology in Villeneuve d’Ascq, France, claim to have built the first ultra-short nitride HEMTs with an AlGaN back barrier. “The uniqueness of this work comes from highly scaled, ultrathin barrier AlN/GaN devices suitable for high frequency GaN-onsilicon operation and high-voltage operation," says lead author Farid Medjdoub.

The AlGaN back-barrier HEMTs, which have a 0.2 μm gate length and a 1 μm separation between the gate and drain, operate at cut-off frequencies in excess of 50 GHz, deliver twice as much current as standard nitride HEMTs and produce a high blocking voltage.

Superiority over standard HEMTs stems from better electron confinement, which allows the transistor to be biased at a higher voltage. Medjdoub and his co-workers fabricated their HEMTs on 4-inch, high-resistivity silicon (111) substrates. MOCVD was used to form a standard HEMT, which acted as a control, and the slightly more complex double heterostructure FET that had an Al0.08Ga0.92N buffer acting as a back barrier.

According to Medjdoub, it is no more difficult to grow a highquality AlGaN buffer than one made of GaN. “In term of growth, the challenge is definitely the achievement of high AlN quality [for the top barrier]. This provides huge polarization and results in extremely high current density," says Medjdoub. He and his coworkers primarily attribute the high-quality of their 6 nm AlN barrier to the in-situ growth of a 3 nm-thick SiN cap that prevents strain relaxation. Ohmic contacts have been formed directly on top of the AlN barrier by etching the SiN layer and depositing a Ti/Al/Ni/Au stack. Nitrogen implantation isolated the devices, and deposition of a 50 nm-thick SiN film by plasma-enhanced CVD, followed by e-beam lithography, defined a 2 μm gate length.

Plasma etching removes SiN under the gate, and electron-beam lithography adds a Ni/Au gate to create transistors with a 50 μm device width and gate-source and gate-drain spacings of 0.3 μm and 1 μm, respectively. These are passivated with a 100 nm-thick film of SiN. Evidence for the improvement in electron confinement with the addition of an AlGaN back-barrier is provided by plots of the drain current verses source-drain voltage (see Figure). The addition of this ternary back barrier enables operation of the device with a drain voltage of 50 V or more.

Introducing the AlGaN barrier also led to an increase in cut-off frequency from 44 GHz to 52 GHz, and a hike in the maximum oscillation frequency from 68 GHz to 91 GHz.The French team has noticed a thermal limitation with the 8 percent aluminium, AlGaN back barrier. “We plan to reduce the aluminium content to less than 5 percent in order to significantly improve the thermal management while maintaining excellent electron confinement," says Medjdoub. “Then, we expect to achieve, for the first time, GaN-on-silicon high power in the millimetre range."






Info
×
Search the news archive

To close this popup you can press escape or click the close icon.
×
Logo
×
Register - Step 1

You may choose to subscribe to the Compound Semiconductor Magazine, the Compound Semiconductor Newsletter, or both. You may also request additional information if required, before submitting your application.


Please subscribe me to:

 

You chose the industry type of "Other"

Please enter the industry that you work in:
Please enter the industry that you work in:
 
X
Info
X
Info
Live Event