Voids boost LED light emission

Higher light extraction efficiency results from a novel architecture formed by laser drilling and photochemical etching
A partnership between researchers in the US and China has increased LED output power by more than one-fifth via the creation of air gaps within the device.To deliver the increase in extraction efficiency, the researchers from National Chung Hsing University and Yale University drilled holes with a laser, before etching a heavily doped GaN layer beneath the LED structure.

Fabrication of these novel LEDs began with growth of an epistructure on sapphire that had a low-temperature buffer, an 1.2µm-thick undoped GaN layer, a heavily doped 0.2µm -thick GaN layer and a 0.2µm-thick undoped GaN layer. On top of this they deposited a relatively conventional device structure, which was capped with a 250 nm-thick layer of the transparent conductive material indium tin oxide.

Engineers employed a 355 nm laser to drill 10µm -diameter holes down to the heavily doped n-type layer, and used an electrochemical wet-etching process to create disk-shaped voids with a diameter of 40µm.

Driven at 20 mA, the etched LED delivered a light output power that was 22 percent higher than that of the control. However, this gain in the output came at the expense of a small increase in operating voltage from 3.12 V to 3.19 V, due to the slightly reduced emission area and the increased resistance of the treated LED structure.

Ref. C. -F. Lin et. al. Appl. Phys. Express 7 076501 (2014)

×
Search the news archive

To close this popup you can press escape or click the close icon.
Logo
x
Logo
×
Register - Step 1

You may choose to subscribe to the Compound Semiconductor Magazine, the Compound Semiconductor Newsletter, or both. You may also request additional information if required, before submitting your application.


Please subscribe me to:

 

You chose the industry type of "Other"

Please enter the industry that you work in:
Please enter the industry that you work in: